16MnCr5 vs 30CrMoV9: 25% composition overlap. Significantly different materials serving different application areas.
16MnCr5 vs 30CrMoV9
Side-by-side chemical composition and mechanical property comparison.
Overview
16MnCr5
1.7131
Low-carbon case-hardening steel with manganese and chromium. Excellent for carburizing to produce a hard, wear-resistant surface with a tough core. Standard choice for gears, camshafts, piston pins, and transmission components.
30CrMoV9
1.7707
THE Cr-Mo-V nitriding steel — Cr 2.3-2.7% forms hard CrN nitrided case (800 HV surface). V addition for secondary hardening. Core QT to UTS 1080-1270 MPa before nitriding at 570-580°C. Used for piston rods, valve stems, cylinder liners, turbine parts, and any component needing extreme surface hardness + fatigue resistance without distortion (low nitriding temp).
| 16MnCr5 | 30CrMoV9 | |
|---|---|---|
| Material Number | 1.7131 | 1.7707 |
| Category | Alloy Steel | Alloy Steel |
| Standard | EN 10084 | EN 10085 |
Chemical composition (wt%)
| Element | 16MnCr5 | 30CrMoV9 | Overlap |
|---|---|---|---|
| C | 0.14–0.19% | 0.26–0.34% | No overlap |
| Si | 0–0.4% | 0–0.4% | OK |
| Mn | 1–1.3% | 0.4–0.7% | No overlap |
| P | 0–0.025% | — | — |
Mechanical properties
| Property | 16MnCr5 | 30CrMoV9 | Unit |
|---|---|---|---|
| tensile_strength | 800–1100 | 1080–1270 | MPa |
| yield_strength | ≥ 590 | ≥ 880 | MPa |
| elongation | ≥ 10 | ≥ 10 | % |
Compatibility Assessment
16MnCr5 and 30CrMoV9 have significantly different compositions (25% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is 16MnCr5 the same as 30CrMoV9?
16MnCr5 and 30CrMoV9 have a 25% composition overlap. They are generally not directly interchangeable.
Can I replace 16MnCr5 with 30CrMoV9?
Generally not recommended. The compositions differ significantly (25% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between 16MnCr5 and 30CrMoV9?
The main differences are in the following elements: C, Mn, Cr. 16MnCr5 is a Alloy Steel grade, while 30CrMoV9 is a Alloy Steel grade.
Related Comparisons
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.