40CrMnMo7 vs HS6-5-2-5: 9% composition overlap. Significantly different materials serving different application areas.
40CrMnMo7 vs HS6-5-2-5
Side-by-side chemical composition and mechanical property comparison.
Overview
40CrMnMo7
1.2311
Pre-hardened plastic mold steel — delivered at 28-32 HRC, ready for machining without further heat treatment. The European equivalent of AISI P20. Cr-Mn-Mo composition for good through-hardenability in large sections. THE workhorse mold base material for injection molds, compression molds, and die casting dies. Good machinability, polishability, and photo-etchability. Used for mold frames, large injection molds, blow molds, and structural die components.
HS6-5-2-5
1.3243
Standard cobalt high speed steel with 5% Co — the most widely used cobalt HSS grade. Also known as M35 or HSS-E/HSSE. Better hot hardness and cutting performance than M2, lower cost than M42. HRC 64-66 hardened. The "go-to upgrade" when M2 performance is insufficient. Used for drill bits (HSS-Co branded), taps, end mills, saw blades, and general-purpose cutting tools for stainless steel and medium-hard alloys.
| 40CrMnMo7 | HS6-5-2-5 | |
|---|---|---|
| Material Number | 1.2311 | 1.3243 |
| Category | Tool Steel | Tool Steel |
| Standard | EN ISO 4957 | EN ISO 4957 |
Chemical composition (wt%)
| Element | 40CrMnMo7 | HS6-5-2-5 | Overlap |
|---|---|---|---|
| C | 0.35–0.45% | 0.86–0.94% | No overlap |
| Si | 0.2–0.4% | 0–0.45% | OK |
| Mn | 1.3–1.6% | 0–0.4% | No overlap |
| P | 0–0.03% | — | — |
Mechanical properties
| Property | 40CrMnMo7 | HS6-5-2-5 | Unit |
|---|---|---|---|
| tensile_strength | 900–1050 | — | MPa |
| yield_strength | 700–800 | — | MPa |
| hardness_hrc | 28–32 | 64–66 | HRC |
Compatibility Assessment
40CrMnMo7 and HS6-5-2-5 have significantly different compositions (9% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is 40CrMnMo7 the same as HS6-5-2-5?
40CrMnMo7 and HS6-5-2-5 have a 9% composition overlap. They are generally not directly interchangeable.
Can I replace 40CrMnMo7 with HS6-5-2-5?
Generally not recommended. The compositions differ significantly (9% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between 40CrMnMo7 and HS6-5-2-5?
The main differences are in the following elements: C, Mn, Cr, Mo. 40CrMnMo7 is a Tool Steel grade, while HS6-5-2-5 is a Tool Steel grade.
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.