C10E vs S275J0: 44% composition overlap. Significantly different materials serving different application areas.
C10E vs S275J0
Side-by-side chemical composition and mechanical property comparison.
Overview
C10E
1.1121
Lowest practical carbon case-hardening steel — 0.07-0.13% C. After carburizing: hard surface (HRC 55-60) with extremely soft, tough core (HRC 15-20). Maximum impact absorption. Modern designation for Ck10. Used for pins, bushings, small gears, camshaft lobes, and any carburized part where maximum core toughness and ductility are critical. Also used as cold-heading and deep-drawing wire/strip.
S275J0
1.0143
Structural steel with guaranteed Charpy impact at 0°C (KV >=27J). Between S235J0 and S355J0 in the strength range. ReH >=275 MPa. Very widely used in European construction: building frames, columns, beams, and general structural applications. Good weldability. Often specified as standard section material (IPE, HEA, UPN profiles).
| C10E | S275J0 | |
|---|---|---|
| Material Number | 1.1121 | 1.0143 |
| Category | Carbon Steel | Carbon Steel |
| Standard | EN 10084 | EN 10025-2 |
Chemical composition (wt%)
| Element | C10E | S275J0 | Overlap |
|---|---|---|---|
| C | 0.07–0.13% | 0–0.18% | OK |
| Si | 0–0.4% | ≥ 0% | OK |
| Mn | 0.3–0.6% | 0–1.5% | OK |
| P | 0–0.025% | 0–0.03% | OK |
Mechanical properties
| Property | C10E | S275J0 | Unit |
|---|---|---|---|
| tensile_strength | 310–440 | 410–560 | MPa |
| yield_strength | 180–220 | ≥ 275 | MPa |
| elongation | 28–35 | ≥ 21 | % |
Compatibility Assessment
C10E and S275J0 have significantly different compositions (44% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is C10E the same as S275J0?
C10E and S275J0 have a 44% composition overlap. They are generally not directly interchangeable.
Can I replace C10E with S275J0?
Generally not recommended. The compositions differ significantly (44% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between C10E and S275J0?
The main differences are in the following elements: overall alloying content. C10E is a Carbon Steel grade, while S275J0 is a Carbon Steel grade.
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.