C22E vs P235GH: 55% composition overlap. Moderate differences, generally not direct substitutes.
C22E vs P235GH
Side-by-side chemical composition and mechanical property comparison.
Overview
C22E
1.1151
Low-carbon unalloyed steel for case hardening and general engineering — 0.17-0.24% C. After carburizing: surface HRC 55-60, soft tough core. Much cheaper than alloy case-hardening steels (16MnCr5, 20MnCr5). Modern designation for Ck22. Used for pins, bolts, levers, lightly loaded gears, and any carburized part where alloy additions are not justified. Also used as cold-heading wire.
P235GH
1.0345
Lowest-strength pressure vessel steel — ReH >=235 MPa. Excellent weldability due to very low C (max 0.16%). THE entry-level boiler/pressure vessel plate in EN 10028-2. Used for low-pressure vessels, boiler drums, heat exchangers, and steam piping at modest pressures and temperatures to ~400°C.
| C22E | P235GH | |
|---|---|---|
| Material Number | 1.1151 | 1.0345 |
| Category | Carbon Steel | Carbon Steel |
| Standard | EN 10083-2 | EN 10028-2 |
Chemical composition (wt%)
| Element | C22E | P235GH | Overlap |
|---|---|---|---|
| C | 0.17–0.24% | 0–0.16% | No overlap |
| Si | 0–0.4% | 0–0.35% | OK |
| Mn | 0.4–0.7% | 0–1.2% | OK |
| P | 0–0.025% | 0–0.025% | OK |
Mechanical properties
| Property | C22E | P235GH | Unit |
|---|---|---|---|
| tensile_strength | 410–540 | 360–480 | MPa |
| yield_strength | 240–280 | ≥ 235 | MPa |
| elongation | 22–28 | ≥ 25 | % |
Compatibility Assessment
C22E and P235GH have moderate differences (55% overlap). They are generally not direct substitutes. Consider the specific requirements of your application.
Automated assessment based on composition analysis
Frequently Asked Questions
Is C22E the same as P235GH?
C22E and P235GH have a 55% composition overlap. They are generally not directly interchangeable.
Can I replace C22E with P235GH?
Generally not recommended. The compositions differ significantly (55% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between C22E and P235GH?
The main differences are in the following elements: C. C22E is a Carbon Steel grade, while P235GH is a Carbon Steel grade.
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.