C22E vs P355GH: 60% composition overlap. Moderate differences, generally not direct substitutes.
C22E vs P355GH
Side-by-side chemical composition and mechanical property comparison.
Overview
C22E
1.1151
Low-carbon unalloyed steel for case hardening and general engineering — 0.17-0.24% C. After carburizing: surface HRC 55-60, soft tough core. Much cheaper than alloy case-hardening steels (16MnCr5, 20MnCr5). Modern designation for Ck22. Used for pins, bolts, levers, lightly loaded gears, and any carburized part where alloy additions are not justified. Also used as cold-heading wire.
P355GH
1.0473
Higher-strength pressure vessel steel — ReH >=355 MPa, guaranteed elevated-temperature properties. Between P265GH and 16Mo3 in the pressure vessel hierarchy. Used for boilers, steam drums, heat exchangers, and pressure piping operating to ~400°C. EN 10028-2, PED 2014/68/EU compliant. Good weldability.
| C22E | P355GH | |
|---|---|---|
| Material Number | 1.1151 | 1.0473 |
| Category | Carbon Steel | Carbon Steel |
| Standard | EN 10083-2 | EN 10028-2 |
Chemical composition (wt%)
| Element | C22E | P355GH | Overlap |
|---|---|---|---|
| C | 0.17–0.24% | 0–0.22% | Partial |
| Si | 0–0.4% | 0–0.4% | OK |
| Mn | 0.4–0.7% | 0–1.6% | OK |
| P | 0–0.025% | 0–0.025% | OK |
Mechanical properties
| Property | C22E | P355GH | Unit |
|---|---|---|---|
| tensile_strength | 410–540 | 490–630 | MPa |
| yield_strength | 240–280 | ≥ 355 | MPa |
| elongation | 22–28 | ≥ 20 | % |
Compatibility Assessment
C22E and P355GH have moderate differences (60% overlap). They are generally not direct substitutes. Consider the specific requirements of your application.
Automated assessment based on composition analysis
Frequently Asked Questions
Is C22E the same as P355GH?
C22E and P355GH have a 60% composition overlap. They are generally not directly interchangeable.
Can I replace C22E with P355GH?
Generally not recommended. The compositions differ significantly (60% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between C22E and P355GH?
The main differences are in the following elements: C. C22E is a Carbon Steel grade, while P355GH is a Carbon Steel grade.
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.