E7018-1 H4R vs ER316L: 41% composition overlap. Significantly different materials serving different application areas.
E7018-1 H4R vs ER316L
Side-by-side chemical composition and mechanical property comparison.
Overview
E7018-1 H4R
Low-hydrogen basic coated SMAW electrode with enhanced toughness (-45°C) and moisture-resistant coating (H4R designation = max 4ml H₂/100g, moisture-resistant). The premium structural steel electrode for critical applications: bridges, high-rise buildings, offshore structures, pressure vessels (ASME Section IX) and seismic-resistant frames. 70 ksi (485 MPa) tensile strength. AC or DCEP. The "-1" suffix indicates 27J impact at -45°C. H4R coating resists moisture pickup for 9+ hours after removal from hermetically sealed packaging.
ER316L
Low-carbon molybdenum-bearing austenitic stainless steel welding wire — the standard filler for joining 316 and 316L stainless steels. 2-3% Mo provides superior pitting and crevice corrosion resistance versus ER308L, especially in chloride environments. Low carbon (≤0.03%) prevents sensitization. Used for TIG and MIG welding of chemical processing equipment, marine hardware, pharmaceutical vessels, pulp & paper digesters, and offshore piping. Also used for dissimilar joints between 304 and 316 grades.
| E7018-1 H4R | ER316L | |
|---|---|---|
| Material Number | — | — |
| Category | Welding | Welding |
| Standard | AWS A5.1 | AWS A5.9 |
Chemical composition (wt%)
| Element | E7018-1 H4R | ER316L | Overlap |
|---|---|---|---|
| C | ≤ 0.08% | ≤ 0.03% | OK |
| Si | 0.3–0.6% | 0.3–0.65% | OK |
| Mn | 1–1.6% | 1–2.5% | OK |
| P | ≤ 0.025% | ≤ 0.03% | OK |
Mechanical properties
| Property | E7018-1 H4R | ER316L | Unit |
|---|---|---|---|
| Tensile Strength | ≥ 485 | — | MPa |
| Yield Strength | ≥ 400 | — | MPa |
| Elongation | ≥ 22 | — | % |
Compatibility Assessment
E7018-1 H4R and ER316L have significantly different compositions (41% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is E7018-1 H4R the same as ER316L?
E7018-1 H4R and ER316L have a 41% composition overlap. They are generally not directly interchangeable.
Can I replace E7018-1 H4R with ER316L?
Generally not recommended. The compositions differ significantly (41% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between E7018-1 H4R and ER316L?
The main differences are in the following elements: Cr, Mo, Ni. E7018-1 H4R is a Welding grade, while ER316L is a Welding grade.
View full data for each material: