Epoxy/Carbon Fiber (CFRP) vs FKM (Fluoroelastomer / Viton): 0% composition overlap. Significantly different materials serving different application areas.
Epoxy/Carbon Fiber (CFRP) vs FKM (Fluoroelastomer / Viton)
Side-by-side chemical composition and mechanical property comparison.
Overview
Epoxy/Carbon Fiber (CFRP)
Carbon fiber reinforced epoxy — the benchmark structural composite material. Unidirectional ply: tensile strength 1500–2000 MPa, modulus 120–150 GPa at density 1.55 g/cm³ (5x stronger than steel at 1/5 the weight). Quasi-isotropic layup: UTS ~600 MPa, E ~50 GPa. Autoclave-cured prepreg (aerospace) or infusion/RTM (industrial). Used in aerospace primary structures (fuselage, wings), Formula 1 chassis, bicycle frames, wind turbine blades, pressure vessels (Type IV) and high-end sporting goods. Fiber types: T300, T700, T800, M40J, M55J.
FKM (Fluoroelastomer / Viton)
Fluoroelastomer — THE high-temperature and chemical-resistant rubber. Outstanding resistance to oils, fuels, acids, and solvents at temperatures up to 200°C (short-term 230°C). Fluorine content (64-70%) determines chemical resistance. Trade names: Viton (Chemours), Tecnoflon (Solvay), Dai-El (Daikin). 5-10x more expensive than NBR. Used for aerospace fuel seals, chemical process seals, automotive fuel injector O-rings, semiconductor processing, and any seal exposed to aggressive chemicals at high temperature.
| Epoxy/Carbon Fiber (CFRP) | FKM (Fluoroelastomer / Viton) | |
|---|---|---|
| Material Number | — | — |
| Category | Polymers | Polymers |
| Standard | ASTM D3039 | ISO 37 |
Mechanical properties
| Property | Epoxy/Carbon Fiber (CFRP) | FKM (Fluoroelastomer / Viton) | Unit |
|---|---|---|---|
| Tensile Strength | 1500–2000 | — | MPa |
| Tensile Modulus | 120–150 | — | GPa |
| Density | 1.5–1.6 | — | g/cm³ |
Compatibility Assessment
Epoxy/Carbon Fiber (CFRP) and FKM (Fluoroelastomer / Viton) have significantly different compositions (0% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is Epoxy/Carbon Fiber (CFRP) the same as FKM (Fluoroelastomer / Viton)?
Epoxy/Carbon Fiber (CFRP) and FKM (Fluoroelastomer / Viton) have a 0% composition overlap. They are generally not directly interchangeable.
Can I replace Epoxy/Carbon Fiber (CFRP) with FKM (Fluoroelastomer / Viton)?
Generally not recommended. The compositions differ significantly (0% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between Epoxy/Carbon Fiber (CFRP) and FKM (Fluoroelastomer / Viton)?
The main differences are in the following elements: overall alloying content. Epoxy/Carbon Fiber (CFRP) is a Polymers grade, while FKM (Fluoroelastomer / Viton) is a Polymers grade.
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.