Epoxy/Carbon Fiber (CFRP) vs PA6 GF30: 0% composition overlap. Significantly different materials serving different application areas.
Epoxy/Carbon Fiber (CFRP) vs PA6 GF30
Side-by-side chemical composition and mechanical property comparison.
Overview
Epoxy/Carbon Fiber (CFRP)
Carbon fiber reinforced epoxy — the benchmark structural composite material. Unidirectional ply: tensile strength 1500–2000 MPa, modulus 120–150 GPa at density 1.55 g/cm³ (5x stronger than steel at 1/5 the weight). Quasi-isotropic layup: UTS ~600 MPa, E ~50 GPa. Autoclave-cured prepreg (aerospace) or infusion/RTM (industrial). Used in aerospace primary structures (fuselage, wings), Formula 1 chassis, bicycle frames, wind turbine blades, pressure vessels (Type IV) and high-end sporting goods. Fiber types: T300, T700, T800, M40J, M55J.
PA6 GF30
Polyamide 6 with 30% short glass fiber reinforcement — the industry standard for metal replacement in structural injection-molded parts. UTS doubles vs unfilled PA6 (175 vs 80 MPa), stiffness triples (E-Mod 9.5 vs 3.0 GPa), and HDT jumps to 200°C+. The classic materialref.com differentiation case: Ultramid B3WG6 (BASF) = Zytel 73G30 (DuPont) = Durethan BKV 30 (LANXESS) = Akulon K224-G6 (DSM) = Grilon BG-30 (EMS) = Technyl C216 V30 (Domo) — all the same base material. Used for automotive brackets, engine covers, power tool housings, electrical connectors, and structural inserts.
| Epoxy/Carbon Fiber (CFRP) | PA6 GF30 | |
|---|---|---|
| Material Number | — | — |
| Category | Polymers | Polymers |
| Standard | ASTM D3039 | ISO 10350 |
Mechanical properties
| Property | Epoxy/Carbon Fiber (CFRP) | PA6 GF30 | Unit |
|---|---|---|---|
| Tensile Strength | 1500–2000 | — | MPa |
| Tensile Modulus | 120–150 | — | GPa |
| Density | 1.5–1.6 | — | g/cm³ |
Compatibility Assessment
Epoxy/Carbon Fiber (CFRP) and PA6 GF30 have significantly different compositions (0% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is Epoxy/Carbon Fiber (CFRP) the same as PA6 GF30?
Epoxy/Carbon Fiber (CFRP) and PA6 GF30 have a 0% composition overlap. They are generally not directly interchangeable.
Can I replace Epoxy/Carbon Fiber (CFRP) with PA6 GF30?
Generally not recommended. The compositions differ significantly (0% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between Epoxy/Carbon Fiber (CFRP) and PA6 GF30?
The main differences are in the following elements: overall alloying content. Epoxy/Carbon Fiber (CFRP) is a Polymers grade, while PA6 GF30 is a Polymers grade.
Related Comparisons
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.