HS6-5-2 vs O1 / 100MnCrW4: 11% composition overlap. Significantly different materials serving different application areas.
HS6-5-2 vs O1 / 100MnCrW4
Side-by-side chemical composition and mechanical property comparison.
Overview
HS6-5-2
1.3343
The most widely used high-speed steel worldwide, known as AISI M2. Contains 6% W, 5% Mo and 2% V providing excellent red hardness (retains cutting ability at 600°C+), high wear resistance and good toughness. Hardened to 62–65 HRC. Standard material for twist drills, milling cutters, taps, reamers, broaches, saw blades, cold forming tools and punches. PM (powder metallurgy) variants available for improved toughness and grindability.
O1 / 100MnCrW4
1.2510
Oil-hardening cold-work tool steel. Good balance of wear resistance, toughness, and machinability at moderate cost. Very predictable heat treatment response. The standard choice for hand tools, gauges, jigs, fixtures, taps, reamers, and general precision tooling.
| HS6-5-2 | O1 / 100MnCrW4 | |
|---|---|---|
| Material Number | 1.3343 | 1.2510 |
| Category | Tool Steel | Tool Steel |
| Standard | EN ISO 4957 | EN ISO 4957 |
Chemical composition (wt%)
| Element | HS6-5-2 | O1 / 100MnCrW4 | Overlap |
|---|---|---|---|
| C | 0.8–0.88% | 0.9–1.05% | No overlap |
| Si | ≤ 0.45% | 0.1–0.4% | OK |
| Mn | ≤ 0.4% | 1–1.2% | No overlap |
| P | ≤ 0.03% | — | — |
Mechanical properties
| Property | HS6-5-2 | O1 / 100MnCrW4 | Unit |
|---|---|---|---|
| Hardness HB | ≤ 255 | — | HB |
| Hardness HRC | 62–65 | — | HRC |
| Density | 8.16 | — | g/cm³ |
Compatibility Assessment
HS6-5-2 and O1 / 100MnCrW4 have significantly different compositions (11% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is HS6-5-2 the same as O1 / 100MnCrW4?
HS6-5-2 and O1 / 100MnCrW4 have a 11% composition overlap. They are generally not directly interchangeable.
Can I replace HS6-5-2 with O1 / 100MnCrW4?
Generally not recommended. The compositions differ significantly (11% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between HS6-5-2 and O1 / 100MnCrW4?
The main differences are in the following elements: C, Mn, Cr, V. HS6-5-2 is a Tool Steel grade, while O1 / 100MnCrW4 is a Tool Steel grade.
View full data for each material: