HS6-5-2 vs X153CrMoV12: 32% composition overlap. Significantly different materials serving different application areas.
HS6-5-2 vs X153CrMoV12
Side-by-side chemical composition and mechanical property comparison.
Overview
HS6-5-2
1.3343
The most widely used high-speed steel worldwide, known as AISI M2. Contains 6% W, 5% Mo and 2% V providing excellent red hardness (retains cutting ability at 600°C+), high wear resistance and good toughness. Hardened to 62–65 HRC. Standard material for twist drills, milling cutters, taps, reamers, broaches, saw blades, cold forming tools and punches. PM (powder metallurgy) variants available for improved toughness and grindability.
X153CrMoV12
1.2379
High-carbon high-chromium ledeburitic cold work tool steel — AISI D2. 12% Cr + 1.5% C forms massive M7C3 carbides giving outstanding wear resistance and cutting edge retention. Air-hardening with minimal distortion. Lower toughness than H13. Used for blanking/stamping dies, thread rolling dies, cold forming tools, slitting cutters, and wear parts. Also popular as high-end knife steel.
| HS6-5-2 | X153CrMoV12 | |
|---|---|---|
| Material Number | 1.3343 | 1.2379 |
| Category | Tool Steel | Tool Steel |
| Standard | EN ISO 4957 | EN ISO 4957 |
Chemical composition (wt%)
| Element | HS6-5-2 | X153CrMoV12 | Overlap |
|---|---|---|---|
| C | 0.8–0.88% | 1.45–1.6% | No overlap |
| Si | ≤ 0.45% | 0.1–0.6% | Partial |
| Mn | ≤ 0.4% | 0.2–0.6% | Partial |
| P | ≤ 0.03% | 0–0.03% | OK |
Mechanical properties
| Property | HS6-5-2 | X153CrMoV12 | Unit |
|---|---|---|---|
| Hardness HB | ≤ 255 | ≤ 255 | HB |
| Hardness HRC | 62–65 | 58–62 | HRC |
| Density | 8.16 | 7.7 | g/cm³ |
Compatibility Assessment
HS6-5-2 and X153CrMoV12 have significantly different compositions (32% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is HS6-5-2 the same as X153CrMoV12?
HS6-5-2 and X153CrMoV12 have a 32% composition overlap. They are generally not directly interchangeable.
Can I replace HS6-5-2 with X153CrMoV12?
Generally not recommended. The compositions differ significantly (32% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between HS6-5-2 and X153CrMoV12?
The main differences are in the following elements: C, Si, Mn, Cr. HS6-5-2 is a Tool Steel grade, while X153CrMoV12 is a Tool Steel grade.
Related Comparisons
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.