M2 / HS6-5-2 vs O1 / 100MnCrW4: 11% composition overlap. Significantly different materials serving different application areas.
M2 / HS6-5-2 vs O1 / 100MnCrW4
Side-by-side chemical composition and mechanical property comparison.
Overview
M2 / HS6-5-2
1.3343
The most widely used high-speed steel worldwide. W-Mo-Cr-V composition gives excellent red hardness (cuts at temperatures up to 600°C). Used for twist drills, end mills, taps, reamers, bandsaw blades, and general-purpose cutting tools. The benchmark HSS grade.
O1 / 100MnCrW4
1.2510
Oil-hardening cold-work tool steel. Good balance of wear resistance, toughness, and machinability at moderate cost. Very predictable heat treatment response. The standard choice for hand tools, gauges, jigs, fixtures, taps, reamers, and general precision tooling.
| M2 / HS6-5-2 | O1 / 100MnCrW4 | |
|---|---|---|
| Material Number | 1.3343 | 1.2510 |
| Category | Tool Steel | Tool Steel |
| Standard | EN ISO 4957 | EN ISO 4957 |
Chemical composition (wt%)
| Element | M2 / HS6-5-2 | O1 / 100MnCrW4 | Overlap |
|---|---|---|---|
| C | 0.8–0.88% | 0.9–1.05% | No overlap |
| Si | 0–0.45% | 0.1–0.4% | OK |
| Mn | 0–0.4% | 1–1.2% | No overlap |
| Cr | 3.8–4.5% | 0.5–0.7% | No overlap |
Mechanical properties
| Property | M2 / HS6-5-2 | O1 / 100MnCrW4 | Unit |
|---|---|---|---|
| hardness_hrc | 63–66 | 57–62 | HRC |
| hardness_hb | ≤ 248 | ≤ 225 | HB |
| e_modulus | ≥ 210 | ≥ 210 | GPa |
Compatibility Assessment
M2 / HS6-5-2 and O1 / 100MnCrW4 have significantly different compositions (11% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is M2 / HS6-5-2 the same as O1 / 100MnCrW4?
M2 / HS6-5-2 and O1 / 100MnCrW4 have a 11% composition overlap. They are generally not directly interchangeable.
Can I replace M2 / HS6-5-2 with O1 / 100MnCrW4?
Generally not recommended. The compositions differ significantly (11% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between M2 / HS6-5-2 and O1 / 100MnCrW4?
The main differences are in the following elements: C, Mn, Cr, V. M2 / HS6-5-2 is a Tool Steel grade, while O1 / 100MnCrW4 is a Tool Steel grade.
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.