100Cr6 vs 16MnCrS5: 25% composition overlap. Significantly different materials serving different application areas.
100Cr6 vs 16MnCrS5
Side-by-side chemical composition and mechanical property comparison.
Overview
100Cr6
1.3505
High-carbon chromium bearing steel. The most widely used bearing steel worldwide. Extremely high hardness and wear resistance after heat treatment. Standard for ball and roller bearings, precision shafts, and measuring instruments.
16MnCrS5
1.7139
Free-cutting variant of 16MnCr5 (1.7131) — sulfur addition (0.020-0.040%) for improved machinability on CNC automatics. Same case-hardening properties: surface 60-62 HRC after carburizing. THE high-volume automotive gear steel where machining cost matters. Used for transmission gears, shafts, pinions, and other carburized parts produced on CNC lathes and multi-spindle automatics.
| 100Cr6 | 16MnCrS5 | |
|---|---|---|
| Material Number | 1.3505 | 1.7139 |
| Category | Alloy Steel | Alloy Steel |
| Standard | EN ISO 683-17 | EN 10084 |
Chemical composition (wt%)
| Element | 100Cr6 | 16MnCrS5 | Overlap |
|---|---|---|---|
| C | 0.93–1.05% | 0.14–0.19% | No overlap |
| Si | 0.15–0.35% | 0–0.4% | OK |
| Mn | 0.25–0.45% | 1–1.3% | No overlap |
| P | 0–0.025% | 0–0.025% | OK |
Mechanical properties
| Property | 100Cr6 | 16MnCrS5 | Unit |
|---|---|---|---|
| hardness_hrc | 60–66 | 60–62 | HRC |
| hardness_hb | ≤ 223 | — | HB |
| e_modulus | ≥ 210 | ≥ 210 | GPa |
Compatibility Assessment
100Cr6 and 16MnCrS5 have significantly different compositions (25% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is 100Cr6 the same as 16MnCrS5?
100Cr6 and 16MnCrS5 have a 25% composition overlap. They are generally not directly interchangeable.
Can I replace 100Cr6 with 16MnCrS5?
Generally not recommended. The compositions differ significantly (25% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between 100Cr6 and 16MnCrS5?
The main differences are in the following elements: C, Mn, S, Cr. 100Cr6 is a Alloy Steel grade, while 16MnCrS5 is a Alloy Steel grade.
Related Comparisons
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.