316 / X5CrNiMo17-12-2 vs 410 / X12Cr13: 52% composition overlap. Moderate differences, generally not direct substitutes.
316 / X5CrNiMo17-12-2 vs 410 / X12Cr13
Side-by-side chemical composition and mechanical property comparison.
Overview
316 / X5CrNiMo17-12-2
1.4401
Standard-carbon austenitic stainless steel with molybdenum. Higher C than 316L (max 0.07% vs 0.03%) giving slightly higher strength. Same corrosion resistance as 316L. Used where welding is not required or post-weld solution annealing is possible.
410 / X12Cr13
1.4006
The basic martensitic stainless steel — 12% chromium with moderate carbon. Hardenable by heat treatment to provide good strength with moderate corrosion resistance. Used for steam turbine blades, pump shafts, valve components, bolts, and mining equipment.
| 316 / X5CrNiMo17-12-2 | 410 / X12Cr13 | |
|---|---|---|
| Material Number | 1.4401 | 1.4006 |
| Category | Stainless Steel | Stainless Steel |
| Standard | EN 10088-2 | EN 10088-2 |
Chemical composition (wt%)
| Element | 316 / X5CrNiMo17-12-2 | 410 / X12Cr13 | Overlap |
|---|---|---|---|
| C | 0–0.07% | 0.08–0.15% | No overlap |
| Si | 0–1% | 0–1% | OK |
| Mn | 0–2% | 0–1.5% | OK |
| P | 0–0.045% | 0–0.04% | OK |
Mechanical properties
| Property | 316 / X5CrNiMo17-12-2 | 410 / X12Cr13 | Unit |
|---|---|---|---|
| tensile_strength | 530–680 | 650–850 | MPa |
| yield_strength | ≥ 220 | ≥ 450 | MPa |
| elongation | ≥ 40 | ≥ 15 | % |
Compatibility Assessment
316 / X5CrNiMo17-12-2 and 410 / X12Cr13 have moderate differences (52% overlap). They are generally not direct substitutes. Consider the specific requirements of your application.
Automated assessment based on composition analysis
Frequently Asked Questions
Is 316 / X5CrNiMo17-12-2 the same as 410 / X12Cr13?
316 / X5CrNiMo17-12-2 and 410 / X12Cr13 have a 52% composition overlap. They are generally not directly interchangeable.
Can I replace 316 / X5CrNiMo17-12-2 with 410 / X12Cr13?
Generally not recommended. The compositions differ significantly (52% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between 316 / X5CrNiMo17-12-2 and 410 / X12Cr13?
The main differences are in the following elements: C, Cr, Ni. 316 / X5CrNiMo17-12-2 is a Stainless Steel grade, while 410 / X12Cr13 is a Stainless Steel grade.
Related Comparisons
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.