630 / 17-4PH vs 15-5PH / X5CrNiCuNb15-5: Both PH stainless — 15-5PH has better transverse toughness
630 / 17-4PH vs 15-5PH / X5CrNiCuNb15-5
Side-by-side chemical composition and mechanical property comparison.
Overview
630 / 17-4PH
1.4542
Precipitation-hardening martensitic stainless steel — the highest-strength stainless in common use. Solution anneal at 1040°C then age at 480-620°C for UTS >1300 MPa. Corrosion resistance similar to 304. Cu+Nb precipitation hardening. Trade names include 17-4PH, SUS630. Used for aerospace structural parts, turbine blades, valve components, nuclear waste casks, medical instruments, and oil/gas equipment.
15-5PH / X5CrNiCuNb15-5
1.4545
Martensitic precipitation-hardening stainless steel. Similar to 17-4PH but with better transverse ductility and toughness due to lower delta ferrite. Used for aerospace structural components, nuclear reactor parts, food processing equipment, and high-performance fasteners.
| 630 / 17-4PH | 15-5PH / X5CrNiCuNb15-5 | |
|---|---|---|
| Material Number | 1.4542 | 1.4545 |
| Category | Stainless Steel | Stainless Steel |
| Standard | EN 10088-3 | AMS 5659 |
Chemical composition (wt%)
| Element | 630 / 17-4PH | 15-5PH / X5CrNiCuNb15-5 | Overlap |
|---|---|---|---|
| C | 0–0.07% | 0–0.07% | OK |
| Si | 0–0.7% | 0–1% | OK |
| Mn | 0–1.5% | 0–1% | OK |
| P | 0–0.04% | 0–0.03% | OK |
Mechanical properties
| Property | 630 / 17-4PH | 15-5PH / X5CrNiCuNb15-5 | Unit |
|---|---|---|---|
| tensile_strength | ≥ 1310 | ≥ 1310 | MPa |
| yield_strength | ≥ 1170 | ≥ 1170 | MPa |
| elongation | ≥ 10 | ≥ 10 | % |
Compatibility Assessment
630 (17-4PH) and 15-5PH have nearly identical strength levels. 15-5PH has higher Ni (5 vs 4%) giving better transverse toughness and more uniform properties. 17-4PH is cheaper and more widely available. Choose 15-5PH for critical aerospace; 17-4PH for general high-strength applications.
Frequently Asked Questions
Is 630 / 17-4PH the same as 15-5PH / X5CrNiCuNb15-5?
630 / 17-4PH and 15-5PH / X5CrNiCuNb15-5 have a 80% composition overlap. Both PH stainless — 15-5PH has better transverse toughness
Can I replace 630 / 17-4PH with 15-5PH / X5CrNiCuNb15-5?
In many cases, yes. The compositions overlap significantly (80%). However, always verify mechanical property requirements and heat treatment compatibility for your specific application.
What is the difference between 630 / 17-4PH and 15-5PH / X5CrNiCuNb15-5?
The main differences are in the following elements: Cr, Ni, Cu. 630 / 17-4PH is a Stainless Steel grade, while 15-5PH / X5CrNiCuNb15-5 is a Stainless Steel grade.
Related Comparisons
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.