Alloy 800H / Incoloy 800H vs Haynes 230: 46% composition overlap. Significantly different materials serving different application areas.
Alloy 800H / Incoloy 800H vs Haynes 230
Side-by-side chemical composition and mechanical property comparison.
Overview
Alloy 800H / Incoloy 800H
1.4958
Iron-nickel-chromium alloy (Fe-32Ni-21Cr) with controlled carbon (0.05–0.10%) and grain size for optimized creep-rupture strength above 600°C. Solution-annealed: Rm ≥450 MPa, Rp0.2 ≥170 MPa, A ≥30%. Density 7.94 g/cm³, E-Modul 196 GPa. Excellent resistance to carburization, oxidation, and nitriding to 1100°C. UNS N08810, ASTM B407/B408/B409. Applications: ethylene cracking tubes, reformer furnace tubes, heat exchangers, nuclear steam generators, chemical reactors. Variant 800HT (N08811/1.4959) has tighter Al+Ti control for even higher creep strength.
Haynes 230
2.4733
Nickel-chromium-tungsten alloy — THE combustor can material for gas turbines. Outstanding oxidation resistance to 1149°C for prolonged exposure. Excellent long-term thermal stability (no sigma/mu phase after 16000h at 649-870°C). Lower thermal expansion than most high-temp alloys. Lanthanum addition improves oxide scale adherence. Used for gas turbine combustion cans, transition ducts, furnace retorts, and catalyst grids in nitric acid production.
| Alloy 800H / Incoloy 800H | Haynes 230 | |
|---|---|---|
| Material Number | 1.4958 | 2.4733 |
| Category | Nickel Alloys | Nickel Alloys |
| Standard | EN 10302 / ASTM B407 | ASTM B435 |
Chemical composition (wt%)
| Element | Alloy 800H / Incoloy 800H | Haynes 230 | Overlap |
|---|---|---|---|
| C | 0.05–0.1% | 0.05–0.1% | OK |
| Si | ≤ 1% | 0.25–0.75% | OK |
| Mn | ≤ 1.5% | 0.3–1% | OK |
| Cr | 19–23% | 20–24% | Partial |
Mechanical properties
| Property | Alloy 800H / Incoloy 800H | Haynes 230 | Unit |
|---|---|---|---|
| density | ≥ 7.94 | ≥ 8.97 | g/cm3 |
| tensile_strength | ≥ 450 | ≥ 760 | MPa |
| yield_strength | ≥ 170 | ≥ 310 | MPa |
Compatibility Assessment
Alloy 800H / Incoloy 800H and Haynes 230 have significantly different compositions (46% overlap). These materials are not interchangeable and serve different application areas.
Automated assessment based on composition analysis
Frequently Asked Questions
Is Alloy 800H / Incoloy 800H the same as Haynes 230?
Alloy 800H / Incoloy 800H and Haynes 230 have a 46% composition overlap. They are generally not directly interchangeable.
Can I replace Alloy 800H / Incoloy 800H with Haynes 230?
Generally not recommended. The compositions differ significantly (46% overlap). These materials have different alloying concepts and are intended for different applications.
What is the difference between Alloy 800H / Incoloy 800H and Haynes 230?
The main differences are in the following elements: Cr, Al, Fe. Alloy 800H / Incoloy 800H is a Nickel Alloys grade, while Haynes 230 is a Nickel Alloys grade.
Related Comparisons
View full data for each material:
Data provided for reference only. Always verify against the applicable specification for critical applications.
All data is for reference only. Equivalents indicate similarity, not identity. Always verify against the applicable specification for safety-critical applications. materialref.com accepts no liability for decisions based on this data.