Crucible Particle Metallurgy high-speed steel with exceptionally high vanadium (4%) and carbon (1.42%) content. Combines the red hardness of M2 HSS with wear resistance approaching carbide. PM process ensures uniform fine carbide distribution impossible in conventional melting. Hardened to 62–66 HRC. Used for end mills, broaches, hobs, form tools, cold heading dies, slitter knives and applications where conventional HSS wears too fast but carbide is too brittle. Popular in knife community for extreme edge retention.

The most widely used high-speed steel worldwide, known as AISI M2. Contains 6% W, 5% Mo and 2% V providing excellent red hardness (retains cutting ability at 600°C+), high wear resistance and good toughness. Hardened to 62–65 HRC. Standard material for twist drills, milling cutters, taps, reamers, broaches, saw blades, cold forming tools and punches. PM (powder metallurgy) variants available for improved toughness and grindability.

Standard cobalt high speed steel with 5% Co — the most widely used cobalt HSS grade. Also known as M35 or HSS-E/HSSE. Better hot hardness and cutting performance than M2, lower cost than M42. HRC 64-66 hardened. The "go-to upgrade" when M2 performance is insufficient. Used for drill bits (HSS-Co branded), taps, end mills, saw blades, and general-purpose cutting tools for stainless steel and medium-hard alloys.

Cobalt super high speed steel — 8% Co for maximum hot hardness (HRC 69 at 550°C). THE HSS for machining superalloys, titanium, and pre-hardened steels where M2 burns out. Mo-series (not W-series like T15). Reaches HRC 68-70 after hardening — among the hardest HSS grades. Also known as HS2-9-1-8 (EN) or SKH59 (JIS). Used for drills, end mills, taps, broaches, and milling cutters for difficult-to-machine materials.